Rutile coated stainless steel electrode for high resistant steels, alloyed / unalloyed steels, heat resistance, Cr-stainless steels including 14% Mn and hard to weld steels. Suitable for dissimilar welding with excellent resistance to thermal shock.
Features and Applications
High resistant steels, alloyed / unalloyed steels, heat-resistant steels, Cr-stainless steels, steels including 14%Mn , hard-to-weld steels
Joint welding and filler welding of difference metal with each other
Electrode coating of rutile character
Austenitic weld metal with resistance to thermal shocks
Maintenance of toughness at temperatures down to -100°C
Requirement of re-drying for min. 2 hours at the temperatures between 120°C and 200°C
Typical Base Material Grades
DIN:X 7 Cr 13, X 7 Cr Al 13, X 10 Cr 13, X 8 Cr 17, X 20 Cr 13, X 10 Cr Al 7, X 10 Cr A 13, X 15 Cr 13, X 22 CrNi 17, X 5 CrNi 134, X 8 CrTi 17, G-X 20 Cr 14, G-X 8 CrNi 13, G-X 30 CrSi 6
AISI: 405, 410, 420, 430, 430 Ti, 431, 440, 502
| Standards |
Current Type |
EN ISO 3581-A - E 18 8 Mn R 32
|
D.C. (+) / A.C.
|
AWS A5.4 - E 307-16
|
|
| Chemical Composition of Weld Metal % (Typical) |
| C |
Si |
Mn |
Ni |
Cr |
| 0.11 |
1.0 |
4.5 |
8.5
|
19.0 |
| Mechanical Properties |
Yield Strength
(N/mm2) |
Tensile Strength
(N/mm2) |
Impact Strength
(ISO-V/+20ºC)
|
Elongation
(Lo=5do)(%) |
min. 390
|
600 - 770
|
min. 47 J |
min. 30
|
Welding Positions
| Operating Data |
| Diameter x Length (mm) |
Welding Current (A) |
Package
Weight (Kg) |
Carton
Weight (Kg) |
|
2.50 x 250
3.20 x 350
4.00 x 350
|
60 - 80
80 - 110
110 - 140
|
3
4.5
4.5
|
12
18
18
|