GeKa SMAW - 310-16|ELOX R Electrode (2.5mm) 3kg

EACH
Availability: In stock
Order Code: 3010101157

Stainless steel electrode used on furnaces, boilers, pipes made of Cr-Ni and Cr-Si-Al alloyed steels with working temperatures up to 1200°C.

 

Features and Applications

Weld metal is resistant to working temperatures up to +1200°C

Used with alternative current also

Requirement of Re-drying for min. 2 hours at the temperatures between 120°C and 200°C

 

Typical Base Material Grades

Furnace, boilers, pipes made of Cr-Ni and Cr-Si-Al-alloyed steels.
X15CrNiSi 25-20, X15CrNiSi 25-21, X15CrNrSi 20-12, G-X40CrNi25, GX40CrNiSi229, X10CrAI,
X10CrAl24, GX40CrSi1, AISI 305, 310, 304


Standards Current Type
EN ISO 3581-A - E 25 20 R 32
D.C. (+) / A.C.
AWS A5.4 - E 310-16
 

 

Chemical Composition of Weld Metal % (Typical)
C Si Mn  Ni Cr
0.12 0.9 2.5 20.0
26.0

 

Mechanical Properties
Yield Strength
(N/mm2)
Tensile Strength
(N/mm2)

Impact Strength
(ISO-V/+20ºC)

Elongation
(Lo=5do)(%)
min. 355
560 - 690
min. 47 J min. 25

 

Welding Positions

 

 

Operating Data
Diameter x Length (mm) Welding Current (A) Package
Weight (Kg)
Carton
Weight (Kg)

2.50 x 250

3.20 x 350

4.00 x 350

50 - 80

80 - 110

110 - 140

3

4.5

4.5

12

18

18

Liability: Whilst all reasonable efforts have been made to ensure the accuracy of the information contained. This information is subject to change without notice and can be only considered as suitable for general guidance.

Stainless steel electrode used on furnaces, boilers, pipes made of Cr-Ni and Cr-Si-Al alloyed steels with working temperatures up to 1200°C.

 

Features and Applications

Weld metal is resistant to working temperatures up to +1200°C

Used with alternative current also

Requirement of Re-drying for min. 2 hours at the temperatures between 120°C and 200°C

 

Typical Base Material Grades

Furnace, boilers, pipes made of Cr-Ni and Cr-Si-Al-alloyed steels.
X15CrNiSi 25-20, X15CrNiSi 25-21, X15CrNrSi 20-12, G-X40CrNi25, GX40CrNiSi229, X10CrAI,
X10CrAl24, GX40CrSi1, AISI 305, 310, 304


Standards Current Type
EN ISO 3581-A - E 25 20 R 32
D.C. (+) / A.C.
AWS A5.4 - E 310-16
 

 

Chemical Composition of Weld Metal % (Typical)
C Si Mn  Ni Cr
0.12 0.9 2.5 20.0
26.0

 

Mechanical Properties
Yield Strength
(N/mm2)
Tensile Strength
(N/mm2)

Impact Strength
(ISO-V/+20ºC)

Elongation
(Lo=5do)(%)
min. 355
560 - 690
min. 47 J min. 25

 

Welding Positions

 

 

Operating Data
Diameter x Length (mm) Welding Current (A) Package
Weight (Kg)
Carton
Weight (Kg)

2.50 x 250

3.20 x 350

4.00 x 350

50 - 80

80 - 110

110 - 140

3

4.5

4.5

12

18

18

Liability: Whilst all reasonable efforts have been made to ensure the accuracy of the information contained. This information is subject to change without notice and can be only considered as suitable for general guidance.