GeKa SMAW - 316L-17|ELOX R Electrode (2.5mm) 3kg

EACH
Availability: In stock
Order Code: 3010101267

Rutile coated low carbon electrode for use in tanks, pipes which are used in the food, textile, chemical and paint industries.

 

Features and Applications

Rutile coated low carbon electrode for use in tanks, pipes and equipment’s made of Cr-Ni-Mo low carbon steels which are used in food, textile, chemical and paint industries

Weld metal is resistant to acid corrosion

Serviceability at temperatures up to 400°C

Requirement of re-drying for min. 2 hours at temperatures between 120°C-200°C

 

Typical Base Material Grades

EN: X10CrNiMoNb 18 12, X2CrNiMo 18 14 3, X5CrNiMo 17 13 3, X2CrNiMo 17 13 2, X2CrNiMoN 17 12 2, X5CrNiMo 17 12 2, X5CrNiMoTi 17 12 2, X6CrNiMoNb 17 12 2, X2CrNiMoN 17 13 3.
AISI: 316Cb, 316, 316L, 316Ti

 

Standards Current Type
EN ISO 3581-A - E 19 12 3 L R 32
D.C. (+) / A.C.
AWS A5.4 - E 316L-17
 

 

Chemical Composition of Weld Metal % (Typical)
C Si Mn  Mo Ni Cr
0.03 0.8 0.9 2.6
11.5 19.0

 

Mechanical Properties
Yield Strength
(N/mm2)
Tensile Strength
(N/mm2)

Impact Strength
(ISO-V/+20ºC)

Elongation
(Lo=5do)(%)
min. 355
540 - 670
min. 47 J min. 30

 

Welding Positions

 

 

Operating Data
Diameter x Length (mm) Welding Current (A) Package
Weight (Kg)
Carton
Weight (Kg)

2.50 x 250

3.20 x 350

4.00 x 350

50 - 90

80 - 120

110 - 160

3

4.5

4.5

12

18

18

Liability: Whilst all reasonable efforts have been made to ensure the accuracy of the information contained. This information is subject to change without notice and can be only considered as suitable for general guidance.

Rutile coated low carbon electrode for use in tanks, pipes which are used in the food, textile, chemical and paint industries.

 

Features and Applications

Rutile coated low carbon electrode for use in tanks, pipes and equipment’s made of Cr-Ni-Mo low carbon steels which are used in food, textile, chemical and paint industries

Weld metal is resistant to acid corrosion

Serviceability at temperatures up to 400°C

Requirement of re-drying for min. 2 hours at temperatures between 120°C-200°C

 

Typical Base Material Grades

EN: X10CrNiMoNb 18 12, X2CrNiMo 18 14 3, X5CrNiMo 17 13 3, X2CrNiMo 17 13 2, X2CrNiMoN 17 12 2, X5CrNiMo 17 12 2, X5CrNiMoTi 17 12 2, X6CrNiMoNb 17 12 2, X2CrNiMoN 17 13 3.
AISI: 316Cb, 316, 316L, 316Ti

 

Standards Current Type
EN ISO 3581-A - E 19 12 3 L R 32
D.C. (+) / A.C.
AWS A5.4 - E 316L-17
 

 

Chemical Composition of Weld Metal % (Typical)
C Si Mn  Mo Ni Cr
0.03 0.8 0.9 2.6
11.5 19.0

 

Mechanical Properties
Yield Strength
(N/mm2)
Tensile Strength
(N/mm2)

Impact Strength
(ISO-V/+20ºC)

Elongation
(Lo=5do)(%)
min. 355
540 - 670
min. 47 J min. 30

 

Welding Positions

 

 

Operating Data
Diameter x Length (mm) Welding Current (A) Package
Weight (Kg)
Carton
Weight (Kg)

2.50 x 250

3.20 x 350

4.00 x 350

50 - 90

80 - 120

110 - 160

3

4.5

4.5

12

18

18

Liability: Whilst all reasonable efforts have been made to ensure the accuracy of the information contained. This information is subject to change without notice and can be only considered as suitable for general guidance.

Product tags