Rutile coated electrode for hardfacing parts on earth and mineral machines, impact drilling and crushing devices, springs, bucket edged and teeth as well as other materials required to have high resistance to wear.
Features and Applications
Electrode covering of rutile character
Usability with a welding transformer (Weldability with AC)
Weld metal with ductile and cracking-resistant behaviours
Requirement of re-drying at the temperature range of 300°C-350°C for 2 hours
Applicability in final layer welding of earth and mineral mining machines. Impact drilling and crushing devices, guide springs, edges of cutting tools, hard manganese steels, bucket edges and teeth
| Standards |
Current Type |
EN 14700 - E Fe 8
|
D.C. (+) / A.C.
|
DIN 8555 - E6-UM-60 P
|
|
| Chemical Composition of Weld Metal % (Typical) |
| C |
Mn |
Si |
Mo |
V |
Cr |
| 0.5 |
0.3 |
1.1 |
1.0 |
1.0 |
7.0 |
| Mechanical Properties |
| Weld Metal Hardness (HRC) |
|
|
|
55 - 59
|
|
|
|
Welding Positions
| Operating Data |
| Diameter x Length (mm) |
Welding Current (A) |
Package
Weight (Kg) |
Carton
Weight (Kg) |
|
3.20 x 350
4.00 x 450
5.00 x 450
|
90 - 135
135 - 180
180 - 230
|
5
6
6
|
15
18
18
|
Liability: Whilst all reasonable efforts have been made to ensure the accuracy of the information contained. This information is subject to change without notice and can be only considered as suitable for general guidance.